Que hàn điện VD-6019

Liên hệ

  • Welding low-carbon steel structures such as ship’s shell, basin, etc.
  • Welded joints without slag bearing and blow holes having shock resistance and endurance bending strength
  • Weld metal revealing few impurities
  • High deposition coefficient

Applied standards

  • QCVN 21:2010/BGTVT MW2
  • ASME/AWS A5.1 E6019
  • EN ISO 2560-A-E 35 2 RA
  • JIS: D4301

Characteristics – applications: 

  • VD – 6019 is the electrode under the group of ilmenite sheath, so the welded joints don’t reveal blow holes or slag bearing. Slags are easily blistered. The well-fined welded joints are ductile, have endurance bending strength and high deposition coefficient.  Possibly welding at all positions.
  • Suitable for welding low-carbon steel under 430 ~ 490 Mpa load with high ductility and bending strength such as rolled-steel structures, ship’s shell, basin, etc.

Chemical composition (%):

C Mn Si P S
Required 0.05~0.13 0.25~0.65 0.05~0.25 ≤ 0.03 ≤ 0.025
Obtained 0.070 0.45 0.12 0.025 0.015

Mechanical property of weld metal:

Yield strength
(Mpa)		 Tensile strength
(Mpa)		 Elongation
(%)		 Shock resistance
(J)		 Bending angle
Required ≥ 331 ≥ 414 ≥ 22 00C: ≥ 47 Not required
Obtained 390 480 27 00C: 80,
t0 phòng: 110		 1500

Instructions for use:

  • Clean oil, grease and dust before welding
  • If the electrode is wet, dry it at 70 ~100 0 C for 30 ~60 minutes before welding
  • Process welding edges as regulated
  • Select appropriate welding current to avoid possible defects
  • Use AC or DC± power
  • Size of the electrode and used current:
Diameter (mm) Φ 4.0 Φ 5.0
Length (mm) 400 400
Amperage (A) Flat welding 160~210 210~250
Vertical welding & Bare welding 130~180 180~230